Heavy Tungsten Alloy Penetrators
Tungsten penetrators, which normally means tungsten alloy (W-Ni-Fe & W-Ni-Cu) penetrators, must withstand the shock incurred while punching through armor plating. Penetrators designed for this purpose have a greatly strengthened case with an especially hardened and shaped nose.
Tungsten penetrators, which normally means tungsten alloy (W-Ni-Fe & W-Ni-Cu) penetrators, must withstand the shock incurred while punching through armor plating. Penetrators designed for this purpose have a greatly strengthened case with an especially hardened and shaped nose.
Name | WNiFe-1 | WNiFe-2 | WNiFe-3 | WNiFe-4 | WNiCu-1 | WNiCu-3 |
Material | 90% W 7% Ni 3% Fe |
92.5% W 5.25% Ni 2.25% Fe |
95% W 3.5% Ni 1.5% Fe |
97% W 2.1% Ni 0.9% Fe |
90% W 6% Ni 4% Cu |
95% W 3.5% Ni 1.5% Cu |
Density (g/cc) | 17 gm/cc | 17.5 gm/cc | 18 gm/cc | 18.5 gm/cc | 17 gm/cc | 18 gm/cc |
Density (lbs/in3) | 0.614 | 0.632 | 0.65 | 0.668 | 0.614 | 0.65 |
Mil. Spec. T-21014 D | Class 1 | Class 2 | Class 3 | Class 4 | Class 1 | Class 3 |
ASTM-B777 | Grade 1 | Grade 2 | Grade 3 | Grade 4 | Grade 1 | Grade 3 |
Type | Type II & III | Type II & III | Type II & III | Type II & III | Type II & III | Type II & III |
Hardness; Rockwell C | 25 | 26 | 27 | 28 | 24 | 27 |
Ultimate Tensile Strength; PSI | 110,000 | 110,000 | 105,000 | 100,000 | 94,000 | 94,000 |
Yield Strength, .2% Offset; PSI | 75,000 | 75,000 | 75,000 | 75,000 | 75,000 | 75,000 |
Elongation, % in 1″ | 5+ | 2+ | 3+ | 2+ | 2+ | 2+ |
Proportional Elastic Limit; PSI | 52,000 | 46,000 | 44,000 | 45,000 | 45,000 | 45,000 |
Modulus of Elasticity; PSI | 45 x 10E6 | 47 x 10E6 | 50 x 10E6 | 53 x 10E6 | 40 x 10E6 | 45 x 10E6 |
Coefficient of Thermal Expansion x 10E-6/°C (20°- 400°C) | 4.8 | 4.6 | 4.6 | 4.5 | 5.4 | 4.4 |
Thermal Conductivity; CGS Units | 0.18 | 0.2 | 0.26 | 0.3 | 0.23 | 0.33 |
Electrical Conductivity; %IACS | 10 | 13 | 13 | 17 | 14 | 16 |
Magnetic Properties | Slightly Magnetic | Slightly Magnetic | Slightly Magnetic | Slightly Magnetic | NIL | NIL |
Tungsten alloy armor-piercing cartridges are available as small arms ammunition, primarily for use as an anti-materiel round, for armored vehicles, concrete bunkers, tanks, and other defenses, depending on the caliber of the firearms. This ammunition consists of a penetrator constructed of tungsten alloy or tungsten carbide, enclosed within a softer jacket, such as copper or aluminum. The product ammunition can range from rifle- and pistol-caliber rounds up to tank rounds.
T&D is an ISO9001:2015 certified domestic supplier of Tungsten Carbide, Heavy Tungsten Alloy, Copper Tungsten, Tungsten, Molybdenum, Tantalum, and Niobium either semifinished blanks or as precision-machined parts. We can deliver your order machined to your specifications as detailed in your technical drawings. Services are available for prototyping and low-to-high-volume production runs.
Modern equipment, low costs, and short lead times allow T&D Materials Manufacture to provide its customers with quality products and excellent customer service. Our capabilities include direct pressing and MIM, CNC pre-forming, HIP sintering to assure consistently high strength, and fully automated CNC finishing to close tolerances and superior finishes.
All our tungsten and tantalum raw materials come from ”Conflict-Free” sources.
ITAR Compliant
T&D Materials Manufacturing Produces all products meeting industry standards of ISO, ASTM, ASM, and MIL as well as custom grades.